Ductility and fracture behavior of cold spray additive manufactured zinc
Publikation: Beiträge in Zeitschriften › Zeitschriftenaufsätze › Forschung › begutachtet
Standard
in: Additive Manufacturing, Jahrgang 89, 104310, 05.06.2024.
Publikation: Beiträge in Zeitschriften › Zeitschriftenaufsätze › Forschung › begutachtet
Harvard
APA
Vancouver
Bibtex
}
RIS
TY - JOUR
T1 - Ductility and fracture behavior of cold spray additive manufactured zinc
AU - Huang, C. J.
AU - Chen, Tara
AU - Fu, Bang Long
AU - Zhang, Z.M.
AU - List, A.
AU - Wiehler, L.
AU - Klusemann, Benjamin
AU - Li, W.Y.
AU - Gärtner, F.
AU - Klassen, Thomas
N1 - Publisher Copyright: © 2024 The Authors
PY - 2024/6/5
Y1 - 2024/6/5
N2 - Tailoring part strength and ductility in additive manufacturing or repair is vital to successful applications. Therefore, applying cold spray as a deposition technique must be tuned for maximum amounts of well-bonded internal interfaces and sufficient softening of the highly work-hardened deposit. With its low melting temperature, Zinc is an ideal model system for studying phenomena associated with high strain rate deformation and local temperature rise effect, both in single impacts and thick deposits. Despite the low temperatures, Zn single splats already show recrystallization at internal interfaces. The respective amounts scale with increasing process gas temperatures. At higher process temperatures, deposits are almost fully recrystallized. The recrystallization obviously improves bonding at internal and at deposit-substrate interfaces. Under optimum conditions, an ultimate deposit strength of up to 135 MPa and an elongation to failure of 18.4 % are reached, comparable to that of laser-manufactured Zn parts. However, the presence of defects in the form of a high density of high-angle grain boundaries and a certain amount of nonbonded splats interfaces results in a lower ductility than that of bulk Zn. This demonstrates a well-tuned interplay between the minimization of defect densities and softening by recrystallization that would allow for deriving bulk-like properties of cold sprayed material without additional post-treatments. Correlations between simulation and experimental results of microstructures, mechanical properties, and fracture mechanisms supply information about the prerequisites for reaching high ductility.
AB - Tailoring part strength and ductility in additive manufacturing or repair is vital to successful applications. Therefore, applying cold spray as a deposition technique must be tuned for maximum amounts of well-bonded internal interfaces and sufficient softening of the highly work-hardened deposit. With its low melting temperature, Zinc is an ideal model system for studying phenomena associated with high strain rate deformation and local temperature rise effect, both in single impacts and thick deposits. Despite the low temperatures, Zn single splats already show recrystallization at internal interfaces. The respective amounts scale with increasing process gas temperatures. At higher process temperatures, deposits are almost fully recrystallized. The recrystallization obviously improves bonding at internal and at deposit-substrate interfaces. Under optimum conditions, an ultimate deposit strength of up to 135 MPa and an elongation to failure of 18.4 % are reached, comparable to that of laser-manufactured Zn parts. However, the presence of defects in the form of a high density of high-angle grain boundaries and a certain amount of nonbonded splats interfaces results in a lower ductility than that of bulk Zn. This demonstrates a well-tuned interplay between the minimization of defect densities and softening by recrystallization that would allow for deriving bulk-like properties of cold sprayed material without additional post-treatments. Correlations between simulation and experimental results of microstructures, mechanical properties, and fracture mechanisms supply information about the prerequisites for reaching high ductility.
KW - Pure zinc
KW - Cold spray additive manufacturing
KW - Recrystallized microstructure
KW - Impact modeling
KW - Mechanical properties
KW - Fracture behavior
KW - Engineering
UR - http://www.scopus.com/inward/record.url?scp=85199063144&partnerID=8YFLogxK
UR - https://www.mendeley.com/catalogue/0e376dac-9e07-3237-aadd-849f7afabe1c/
U2 - 10.1016/j.addma.2024.104310
DO - 10.1016/j.addma.2024.104310
M3 - Journal articles
VL - 89
JO - Additive Manufacturing
JF - Additive Manufacturing
SN - 2214-8604
M1 - 104310
ER -