Ductility and fracture behavior of cold spray additive manufactured zinc

Publikation: Beiträge in ZeitschriftenZeitschriftenaufsätzeForschungbegutachtet

Authors

  • C. J. Huang
  • Tara Chen
  • Bang Long Fu
  • Z.M. Zhang
  • A. List
  • L. Wiehler
  • Benjamin Klusemann
  • W.Y. Li
  • F. Gärtner
  • Thomas Klassen
Tailoring part strength and ductility in additive manufacturing or repair is vital to successful applications. Therefore, applying cold spray as a deposition technique must be tuned for maximum amounts of well-bonded internal interfaces and sufficient softening of the highly work-hardened deposit. With its low melting temperature, Zinc is an ideal model system for studying phenomena associated with high strain rate deformation and local temperature rise effect, both in single impacts and thick deposits. Despite the low temperatures, Zn single splats already show recrystallization at internal interfaces. The respective amounts scale with increasing process gas temperatures. At higher process temperatures, deposits are almost fully recrystallized. The recrystallization obviously improves bonding at internal and at deposit-substrate interfaces. Under optimum conditions, an ultimate deposit strength of up to 135 MPa and an elongation to failure of 18.4 % are reached, comparable to that of laser-manufactured Zn parts. However, the presence of defects in the form of a high density of high-angle grain boundaries and a certain amount of nonbonded splats interfaces results in a lower ductility than that of bulk Zn. This demonstrates a well-tuned interplay between the minimization of defect densities and softening by recrystallization that would allow for deriving bulk-like properties of cold sprayed material without additional post-treatments. Correlations between simulation and experimental results of microstructures, mechanical properties, and fracture mechanisms supply information about the prerequisites for reaching high ductility.
OriginalspracheEnglisch
Aufsatznummer104310
ZeitschriftAdditive Manufacturing
Jahrgang89
Anzahl der Seiten16
ISSN2214-8604
DOIs
PublikationsstatusErschienen - 05.06.2024

Bibliographische Notiz

Publisher Copyright:
© 2024 The Authors

    Fachgebiete

  • Pure zinc, Cold spray additive manufacturing, Recrystallized microstructure, Impact modeling, Mechanical properties, Fracture behavior
  • Ingenieurwissenschaften

DOI

Zuletzt angesehen

Publikationen

  1. Eigene Wege entdecken - Das Linzer Konzept der Klassenführung
  2. "Malerei der Blindheit"
  3. Umweltmanagement und Shareholder Value in den Kriterien des Unternehmenserfolgs
  4. Strategising solidarity
  5. The economic insurance value of ecosystem resilience
  6. Ein neuer Klassenkampf?
  7. Bionik
  8. Sustainable development through aesthetic expertise?
  9. Law, democracy, and the state of emergency.
  10. Mastering the Energy Transition
  11. Mapping the European Commission Today
  12. Immanent/Economic Trinity
  13. Disparate disziplinäre Logiken pädagogischer Handlungsfelder
  14. Effects of heavy resistance training on strength and power in upper extremities in wheelchair athletes
  15. Archive des Digitalen
  16. Higher Education for Sustainable Development.
  17. Psychological approaches to entrepreneurial success
  18. Increasing the Agility of IT Delivery
  19. What are community energy companies trying to accomplish? An empirical investigation of investment motives in the German case
  20. Vorwort
  21. Risk or Resilience? The Role of Trade Integration and Foreign Ownership for the Survival of German Enterprises during the Crisis 2008-2010
  22. The affective shift model of work engagement
  23. Gute Aufgaben im Mathematikunterricht der Grundschule
  24. Tausch, Technik, Krieg
  25. Land use changes and ground dwelling beetle conservation in extensive grazing dehesa systems of north-west Spain
  26. A new constitution for a new Germany
  27. Lebensqualitätsmess-instrumente in der Reha-bilitation Unfallverletzter
  28. Der Künstler als Lehrer
  29. Intentions and synergies the cases of control and speed comment on Di Paolo's 'interactive time travel'
  30. Forschendes Lernen auf Hochschul- und Unterrichtsebene beforschen
  31. Paul Paolucci. Marx’s Experiments and Microscopes: Modes of Production, Religion, and the Method of Successive Abstractions