CaO dissolution during melting and solidification of a Mg-10 wt.% CaO alloy detected with in situ synchrotron radiation diffraction

B. Wiese; C. L. Mendis; D. Tolnai; A. Stark; N. Schell; H. P. Reichel; R. Brückner; K. U. Kainer; N. Hort

doi:10.1016/j.jallcom.2014.08.151

CaO dissolution during melting and solidification of a Mg-10 wt.% CaO alloy detected with in situ synchrotron radiation diffraction

Research output: Journal contributions › Other (editorial matter etc.) › Research

Standard

CaO dissolution during melting and solidification of a Mg-10 wt.% CaO alloy detected with in situ synchrotron radiation diffraction. / Wiese, B.; Mendis, C. L.; Tolnai, D. et al.

In: Journal of Alloys and Compounds, Vol. 618, 05.01.2015, p. 64-66.

Research output: Journal contributions › Other (editorial matter etc.) › Research

Bibtex

@article{adcf11caa4024703bbf3b09769e91666,

title = "CaO dissolution during melting and solidification of a Mg-10 wt.% CaO alloy detected with in situ synchrotron radiation diffraction",

abstract = "The phase dissolution and evolution during the melting and the solidification of Mg containing 10 wt.% CaO was investigated in the temperature range of 20-680 °C. The dissolution of CaO and the formation of Mg2Ca were detected with in situ synchrotron radiation diffraction. The dissolution of CaO was observed at ∼407 °C with the detection of a peak unique to the Mg2Ca phase prior to melting of Mg. After the solidification no CaO was detected, and Mg2Ca and MgO phases were observed.",

keywords = "In situ phase evolution, Liquid-solid reactions, Magnesium alloys, Solidification, Synchrotron radiation, Engineering",

author = "B. Wiese and Mendis, {C. L.} and D. Tolnai and A. Stark and N. Schell and Reichel, {H. P.} and R. Br{\"u}ckner and Kainer, {K. U.} and N. Hort",

year = "2015",

month = jan,

day = "5",

doi = "10.1016/j.jallcom.2014.08.151",

language = "English",

volume = "618",

pages = "64--66",

journal = "Journal of Alloys and Compounds",

issn = "0925-8388",

publisher = "Elsevier B.V.",

}

RIS

TY - JOUR

T1 - CaO dissolution during melting and solidification of a Mg-10 wt.% CaO alloy detected with in situ synchrotron radiation diffraction

AU - Wiese, B.

AU - Mendis, C. L.

AU - Tolnai, D.

AU - Stark, A.

AU - Schell, N.

AU - Reichel, H. P.

AU - Brückner, R.

AU - Kainer, K. U.

AU - Hort, N.

PY - 2015/1/5

Y1 - 2015/1/5

N2 - The phase dissolution and evolution during the melting and the solidification of Mg containing 10 wt.% CaO was investigated in the temperature range of 20-680 °C. The dissolution of CaO and the formation of Mg2Ca were detected with in situ synchrotron radiation diffraction. The dissolution of CaO was observed at ∼407 °C with the detection of a peak unique to the Mg2Ca phase prior to melting of Mg. After the solidification no CaO was detected, and Mg2Ca and MgO phases were observed.

AB - The phase dissolution and evolution during the melting and the solidification of Mg containing 10 wt.% CaO was investigated in the temperature range of 20-680 °C. The dissolution of CaO and the formation of Mg2Ca were detected with in situ synchrotron radiation diffraction. The dissolution of CaO was observed at ∼407 °C with the detection of a peak unique to the Mg2Ca phase prior to melting of Mg. After the solidification no CaO was detected, and Mg2Ca and MgO phases were observed.

KW - In situ phase evolution

KW - Liquid-solid reactions

KW - Magnesium alloys

KW - Solidification

KW - Synchrotron radiation

KW - Engineering

UR - http://www.scopus.com/inward/record.url?scp=84907087664&partnerID=8YFLogxK

U2 - 10.1016/j.jallcom.2014.08.151

DO - 10.1016/j.jallcom.2014.08.151

M3 - Other (editorial matter etc.)

AN - SCOPUS:84907087664

VL - 618

SP - 64

EP - 66

JO - Journal of Alloys and Compounds

JF - Journal of Alloys and Compounds

SN - 0925-8388

ER -

Related by journal

Development of high strength-ductility Mg-Er extruded alloys by micro-alloying with Mn

Zhou, S., Tang, A., Liu, T., Huang, Y., Peng, P., Zhang, J., Hort, N., Willumeit-Römer, R. & Pan, F., 25.06.2023, In: Journal of Alloys and Compounds. 947, 169669.