Nucleation kinetics of the γ-phase in a binary Mg-Al alloy
Research output: Contributions to collected editions/works › Article in conference proceedings › Research › peer-review
Authors
The binary magnesium-aluminum system has been studied extensively the last decades. Surprisingly, the kinetics of nucleation of the γ-precipitates (Mg17Al12) in the α-matrix have not been determined experimentally in detail. The main goal of this research is to investigate the precipitation kinetics of the γ-phase in a Mg-Al alloy during annealing, and to understand the relation between the precipitate volume fraction and the mechanical properties of the material. Comprehensive microstructural analysis was undertaken to reveal the number density, volume fraction, and morphological changes of the γ-precipitates after solution heat treatment (homogenization) and during subsequent annealing below the solvus temperature. As a result, the incubation time and steady state nucleation rate of γ-precipitates in the α-matrix were determined by fitting the experimental data to the classical nucleation theory.
| Original language | English |
|---|---|
| Title of host publication | Magnesium Technology 2013 - Held During the TMS 2013 Annual Meeting and Exhibition |
| Editors | Norbert Hort, Suveen Mathaudhu, Neale Neelameggham, Martyn Alderman |
| Number of pages | 4 |
| Publisher | The Minerals, Metals & Materials Society |
| Publication date | 2013 |
| Pages | 259-262 |
| ISBN (Print) | 978-1-118-60552-3, 978-3-319-48149-4 |
| ISBN (Electronic) | 978-3-319-48150-0 |
| DOIs | |
| Publication status | Published - 2013 |
| Externally published | Yes |
| Event | 142nd Annual Meeting and Exhibition of the Magnesium Technology 2013 - TMS 2013 - San Antonio, TX, United States Duration: 03.03.2013 → 07.03.2013 Conference number: 142 https://www.tms.org/meetings/annual-13/AM13news.aspx?id=4911 |
- Mg-Al alloys, Nucleation kinetics, Precipitation
- Engineering