Microstructural approaches of engineering materials: Influences of Dy content and heat treatments on the formation of hydrides in Mg-Dy alloys
Research output: Contributions to collected editions/works › Article in conference proceedings › Research › peer-review
Standard
Engineering Against Failure - Proceedings of the 3rd International Conference of Engineering Against Failure, ICEAF 2013. University of Patras, 2013. p. 971-980 (Engineering Against Failure - Proceedings of the 3rd International Conference of Engineering Against Failure, ICEAF 2013).
Research output: Contributions to collected editions/works › Article in conference proceedings › Research › peer-review
Harvard
APA
Vancouver
Bibtex
}
RIS
TY - CHAP
T1 - Microstructural approaches of engineering materials
T2 - 3rd International Conference of Engineering Against Failure - ICEAF 2013
AU - Huang, Yuanding
AU - Yang, Lei
AU - Wang, Zhi
AU - Kainer, Karl Ulrich
AU - Hort, Norbert
N1 - Conference code: 3
PY - 2013
Y1 - 2013
N2 - Mg-Dy alloys show promising for being developed as biodegradable medical applications. It is found that the hydride DyH2 could be formed on their surface during their sample preparations. The formation of hydrides in Mg-Dy alloys is affected by the content of Dy and heat treatments. The amount of hydride DyH2 increases with the increment of Dy content. Their formation mechanism is attributed to the surface reaction of Mg-Dy alloys with water. The part of Dy in solid solution plays an important role in influencing the formation of hydrides.
AB - Mg-Dy alloys show promising for being developed as biodegradable medical applications. It is found that the hydride DyH2 could be formed on their surface during their sample preparations. The formation of hydrides in Mg-Dy alloys is affected by the content of Dy and heat treatments. The amount of hydride DyH2 increases with the increment of Dy content. Their formation mechanism is attributed to the surface reaction of Mg-Dy alloys with water. The part of Dy in solid solution plays an important role in influencing the formation of hydrides.
KW - Heat treatment
KW - Hydride
KW - Magnesium alloy
KW - Microstructure
KW - Engineering
UR - http://www.scopus.com/inward/record.url?scp=84905687027&partnerID=8YFLogxK
M3 - Article in conference proceedings
AN - SCOPUS:84905687027
SN - 9789608810433
T3 - Engineering Against Failure - Proceedings of the 3rd International Conference of Engineering Against Failure, ICEAF 2013
SP - 971
EP - 980
BT - Engineering Against Failure - Proceedings of the 3rd International Conference of Engineering Against Failure, ICEAF 2013
PB - University of Patras
Y2 - 26 June 2013 through 28 June 2013
ER -