Microstructural approaches of engineering materials: Influences of Dy content and heat treatments on the formation of hydrides in Mg-Dy alloys

Publikation: Beiträge in SammelwerkenAufsätze in KonferenzbändenForschungbegutachtet

Standard

Microstructural approaches of engineering materials: Influences of Dy content and heat treatments on the formation of hydrides in Mg-Dy alloys. / Huang, Yuanding; Yang, Lei; Wang, Zhi et al.
Engineering Against Failure - Proceedings of the 3rd International Conference of Engineering Against Failure, ICEAF 2013. University of Patras, 2013. S. 971-980 (Engineering Against Failure - Proceedings of the 3rd International Conference of Engineering Against Failure, ICEAF 2013).

Publikation: Beiträge in SammelwerkenAufsätze in KonferenzbändenForschungbegutachtet

Harvard

Huang, Y, Yang, L, Wang, Z, Kainer, KU & Hort, N 2013, Microstructural approaches of engineering materials: Influences of Dy content and heat treatments on the formation of hydrides in Mg-Dy alloys. in Engineering Against Failure - Proceedings of the 3rd International Conference of Engineering Against Failure, ICEAF 2013. Engineering Against Failure - Proceedings of the 3rd International Conference of Engineering Against Failure, ICEAF 2013, University of Patras, S. 971-980, 3rd International Conference of Engineering Against Failure - ICEAF 2013, Kos, Griechenland, 26.06.13.

APA

Huang, Y., Yang, L., Wang, Z., Kainer, K. U., & Hort, N. (2013). Microstructural approaches of engineering materials: Influences of Dy content and heat treatments on the formation of hydrides in Mg-Dy alloys. In Engineering Against Failure - Proceedings of the 3rd International Conference of Engineering Against Failure, ICEAF 2013 (S. 971-980). (Engineering Against Failure - Proceedings of the 3rd International Conference of Engineering Against Failure, ICEAF 2013). University of Patras.

Vancouver

Huang Y, Yang L, Wang Z, Kainer KU, Hort N. Microstructural approaches of engineering materials: Influences of Dy content and heat treatments on the formation of hydrides in Mg-Dy alloys. in Engineering Against Failure - Proceedings of the 3rd International Conference of Engineering Against Failure, ICEAF 2013. University of Patras. 2013. S. 971-980. (Engineering Against Failure - Proceedings of the 3rd International Conference of Engineering Against Failure, ICEAF 2013).

Bibtex

@inbook{d5c884dedcb6448abc667ad7ea916632,
title = "Microstructural approaches of engineering materials: Influences of Dy content and heat treatments on the formation of hydrides in Mg-Dy alloys",
abstract = "Mg-Dy alloys show promising for being developed as biodegradable medical applications. It is found that the hydride DyH2 could be formed on their surface during their sample preparations. The formation of hydrides in Mg-Dy alloys is affected by the content of Dy and heat treatments. The amount of hydride DyH2 increases with the increment of Dy content. Their formation mechanism is attributed to the surface reaction of Mg-Dy alloys with water. The part of Dy in solid solution plays an important role in influencing the formation of hydrides.",
keywords = "Heat treatment, Hydride, Magnesium alloy, Microstructure, Engineering",
author = "Yuanding Huang and Lei Yang and Zhi Wang and Kainer, {Karl Ulrich} and Norbert Hort",
year = "2013",
language = "English",
isbn = "9789608810433",
series = "Engineering Against Failure - Proceedings of the 3rd International Conference of Engineering Against Failure, ICEAF 2013",
publisher = "University of Patras",
pages = "971--980",
booktitle = "Engineering Against Failure - Proceedings of the 3rd International Conference of Engineering Against Failure, ICEAF 2013",
address = "Greece",
note = "3rd International Conference of Engineering Against Failure - ICEAF 2013, ICEAF2013 ; Conference date: 26-06-2013 Through 28-06-2013",

}

RIS

TY - CHAP

T1 - Microstructural approaches of engineering materials

T2 - 3rd International Conference of Engineering Against Failure - ICEAF 2013

AU - Huang, Yuanding

AU - Yang, Lei

AU - Wang, Zhi

AU - Kainer, Karl Ulrich

AU - Hort, Norbert

N1 - Conference code: 3

PY - 2013

Y1 - 2013

N2 - Mg-Dy alloys show promising for being developed as biodegradable medical applications. It is found that the hydride DyH2 could be formed on their surface during their sample preparations. The formation of hydrides in Mg-Dy alloys is affected by the content of Dy and heat treatments. The amount of hydride DyH2 increases with the increment of Dy content. Their formation mechanism is attributed to the surface reaction of Mg-Dy alloys with water. The part of Dy in solid solution plays an important role in influencing the formation of hydrides.

AB - Mg-Dy alloys show promising for being developed as biodegradable medical applications. It is found that the hydride DyH2 could be formed on their surface during their sample preparations. The formation of hydrides in Mg-Dy alloys is affected by the content of Dy and heat treatments. The amount of hydride DyH2 increases with the increment of Dy content. Their formation mechanism is attributed to the surface reaction of Mg-Dy alloys with water. The part of Dy in solid solution plays an important role in influencing the formation of hydrides.

KW - Heat treatment

KW - Hydride

KW - Magnesium alloy

KW - Microstructure

KW - Engineering

UR - http://www.scopus.com/inward/record.url?scp=84905687027&partnerID=8YFLogxK

M3 - Article in conference proceedings

AN - SCOPUS:84905687027

SN - 9789608810433

T3 - Engineering Against Failure - Proceedings of the 3rd International Conference of Engineering Against Failure, ICEAF 2013

SP - 971

EP - 980

BT - Engineering Against Failure - Proceedings of the 3rd International Conference of Engineering Against Failure, ICEAF 2013

PB - University of Patras

Y2 - 26 June 2013 through 28 June 2013

ER -

Zuletzt angesehen

Publikationen

  1. Intermetallic phase characteristics in the Mg–Nd–Zn system
  2. Does Internet-based guided self-help for depression cause harm?
  3. Print exposure across the reading life span
  4. Reaching for the (Product) Stars
  5. Influence of cerium on stress corrosion cracking in AZ91D
  6. Elution of Monomers from Two Conventional Dental Composite Materials
  7. Effects of introspective vs. extraspective instruction in scaling of hedonic properties of flavouring ingredients by Chinese and German subjects
  8. Simulation of the quench sensitivity of the aluminum alloy 6082
  9. Generalising IRT to Discriminate Between Examinees
  10. Systematic study of the effect of non-uniform seal stiffness on the contact stress in flat-faced soft-seated spring operated pressure relief valves
  11. Accurate welding line prediction in extrusion processes
  12. Photochemistry of 2,2', 4,4', %,5'-hexabde (BDE-153) in THF and adsorbed on SiO2
  13. Cues from Facial Expressions for Emotional Interfaces
  14. Manufacture of profiles with variable cross-sections, curvatures and twistings by influencing the material flow in hot extrusion
  15. Effects of habitat heterogeneity on bird communities in forests of northeastern Germany
  16. The multipole resonance probe
  17. German multiple-product, multiple-destination exporters: Bernard-Redding-Schott under test
  18. Forestry contributed to warming of forest ecosystems in northern Germany during the extreme summers of 2018 and 2019
  19. In Situ Synchrotron Radiation Study of the Tension–Compression Asymmetry in an Extruded Mg–2Y–1Zn–1Mn Alloy
  20. Entrepreneurial Traits and Strategy in the Performance of Owner-manager Led Firms
  21. Beyond Personalization and Anonymity:
  22. The effect of hunting regimes on tree regeneration in lowland beech (Fagus sylvatica L.) forests
  23. „Willst du wirklich ,lehren‘ oder ,Lehrer werden‘?“