Comparison on Hot Tearing Behavior of Binary Mg–Al, Mg–Y, Mg–Gd, Mg–Zn, and Mg–Ca Alloys

Publikation: Beiträge in ZeitschriftenZeitschriftenaufsätzeForschungbegutachtet

Authors

  • Jiangfeng Song
  • Hua Zhao
  • Jinge Liao
  • Bin Jiang
  • Ang Zhang
  • Yuanding Huang
  • Karl Ulrich Kainer
  • Norbert Hort
  • Fusheng Pan

Mg–1Al, Mg–0.9Y, Mg–2Gd, Mg–1.5Zn, and Mg–0.5Ca binary alloys were chosen to clarify the hot tearing mechanism since they exhibited the highest hot tearing susceptibility (HTS) among each binary alloy systems. Hot tearing tests of these five binary magnesium alloys were carried out by a constrained rod-casting apparatus. 3D X-ray tomography technology was used to characterize their tear volume, tear patterns, and propagation paths of such tears. The results showed that the HTS of these five alloys followed Mg–1Al < Mg–0.9Y < Mg–2Gd < Mg–1.5Zn < Mg–0.5Ca order. Among them, Mg–0.5Ca alloy exhibited abnormal HTS because of its susceptible temperature range and residual liquid fraction. In addition to the previous analysis of hot tearing behavior, discussion from the point of view of fluidity, thermal expansion coefficient, and mechanical property of semi-solid alloy with high solid fraction were incorporated to clarify the hot tearing mechanism.

OriginalspracheEnglisch
ZeitschriftMetallurgical and Materials Transactions A: Physical Metallurgy and Materials Science
Jahrgang53
Ausgabenummer8
Seiten (von - bis)2986-3001
Anzahl der Seiten16
ISSN1073-5623
DOIs
PublikationsstatusErschienen - 08.2022

DOI