Solid solution treatment on strength and corrosion of biodegradable Mg6Ag wires

Publikation: Beiträge in ZeitschriftenZeitschriftenaufsätzeForschungbegutachtet


  • P. Maier
  • F. Zimmermann
  • M. Rinne
  • G. Szakács
  • N. Hort
  • C. Vogt

A warm-drawn Mg6Ag wire with a diameter of 1.6 mm is investigated by immersion tests in Ringer solution in two conditions: as-drawn and solution heat-treated wire. The initial as-drawn condition showed higher strength in comparison to the solution heat-treated one. As-drawn wire has heavily twinned grains. Heat treatment causes slight grain growth, but less microgalvanic corrosion due to dissolved second phases and a significantly reduction of twin boundaries. The mean corrosion rate decreases by more than half by the heat treatment resulting in higher remaining mechanical properties. The mean corrosion rate also decreases with corrosion time, slightly more for the heat-treated condition. Pitting corrosion was still present after solution heat treatment, although the pit shape is less harmful. The corroded wires and corrosion products were analysed qualitatively and quantitatively by SEM imaging and ICP-OES with focus on the exposure time. Mg6Ag wires corrode under forming Mg(OH)2, CaCO3 and AgCl, SEM imaging proves higher corrosion resistance of heat-treated Mg6Ag. Chemical analysis of wires, corrosion products and corrosion media offer to describe the time-dependent mechanism.

ZeitschriftMaterials and Corrosion
Seiten (von - bis)178-190
Anzahl der Seiten13
PublikationsstatusErschienen - 01.02.2018
Extern publiziertJa