Microstructure, mechanical properties and fracture behaviors of large-scale sand-cast Mg-3Y-2Gd-1Nd-0.4Zr alloy

Publikation: Beiträge in ZeitschriftenZeitschriftenaufsätzeForschungbegutachtet

Standard

Microstructure, mechanical properties and fracture behaviors of large-scale sand-cast Mg-3Y-2Gd-1Nd-0.4Zr alloy. / Yang, Lixiang; Huang, Yuanding; Hou, Zhengquan et al.
in: Journal of Magnesium and Alloys, Jahrgang 11, Nr. 8, 01.08.2023, S. 2763-2775.

Publikation: Beiträge in ZeitschriftenZeitschriftenaufsätzeForschungbegutachtet

Harvard

APA

Vancouver

Yang L, Huang Y, Hou Z, Xiao L, Xu Y, Dong X et al. Microstructure, mechanical properties and fracture behaviors of large-scale sand-cast Mg-3Y-2Gd-1Nd-0.4Zr alloy. Journal of Magnesium and Alloys. 2023 Aug 1;11(8):2763-2775. Epub 2021 Sep 5. doi: 10.1016/j.jma.2021.08.010

Bibtex

@article{fe7a87b78a1a4103bdeb6a1a30b14b61,
title = "Microstructure, mechanical properties and fracture behaviors of large-scale sand-cast Mg-3Y-2Gd-1Nd-0.4Zr alloy",
abstract = "In order to improve the ductility of commercial WE43 alloy and reduce its cost, a Mg-3Y-2Gd-1Nd-0.4Zr alloy with a low amount of rare earths was developed and prepared by sand casting with a differential pressure casting system. Its microstructure, mechanical properties and fracture behaviors in the as-cast, solution-treated and as-aged states were evaluated. It is found that the aged alloy exhibited excellent comprehensive mechanical properties owing to the fine dense plate-shaped β' precipitates formed on prismatic habits during aging at 200 °C for 192 hrs after solution-treated at 500 °C for 24 hrs. Its ultimate tensile strength, yield strength, and elongation at ambient temperature reach to 319 ± 10 MPa, 202 ± 2 MPa and 8.7 ± 0.3% as well as 230 ± 4 MPa, 155 ± 1 MPa and 16.0 ± 0.5% at 250 °C. The fracture mode of as-aged alloy was transferred from cleavage at room temperature to quasi-cleavage and ductile fracture at the test temperature 300 °C. The properties of large-scale components fabricated using the developed Mg-3Y-2Gd-1Nd-0.4Zr alloy are better than those of commercial WE43 alloy, suggesting that the new developed alloy is a good candidate to fabricate the large complex thin-walled components.",
keywords = "Ductility, Large-scale sand-cast, Magnesium alloy, WE43, Engineering",
author = "Lixiang Yang and Yuanding Huang and Zhengquan Hou and Lv Xiao and Yuling Xu and Xiwang Dong and Fei Li and Gerrit Kurz and Baode Sun and Zhongquan Li and Norbert Hort",
note = "This work was funded by the National Natural Science Foundation of China (No. U2037601 and No. 52074183). The authors appreciate Ge Chen, Wenbin Zou as well as Shiwei Wang for preparing the alloys, Wenyu Liu as well as Xuehao Zheng from ZKKF(Beijing) Science & Technology Co. Ltd for the TEM measurement, Gert Wiese as well as Petra Fischer for SEM and hardness measurement and Yunting Li from the Instrument Analysis Center of Shanghai Jiao Tong University (China) for SEM measurement. Lixiang Yang also gratefully thanks the China Scholarship Council (201906230111) for awarding a fellowship to support his study stay at Helmholtz-Zentrum Geesthacht.",
year = "2023",
month = aug,
day = "1",
doi = "10.1016/j.jma.2021.08.010",
language = "English",
volume = "11",
pages = "2763--2775",
journal = "Journal of Magnesium and Alloys",
issn = "2213-9567",
publisher = "Chongqing University",
number = "8",

}

RIS

TY - JOUR

T1 - Microstructure, mechanical properties and fracture behaviors of large-scale sand-cast Mg-3Y-2Gd-1Nd-0.4Zr alloy

AU - Yang, Lixiang

AU - Huang, Yuanding

AU - Hou, Zhengquan

AU - Xiao, Lv

AU - Xu, Yuling

AU - Dong, Xiwang

AU - Li, Fei

AU - Kurz, Gerrit

AU - Sun, Baode

AU - Li, Zhongquan

AU - Hort, Norbert

N1 - This work was funded by the National Natural Science Foundation of China (No. U2037601 and No. 52074183). The authors appreciate Ge Chen, Wenbin Zou as well as Shiwei Wang for preparing the alloys, Wenyu Liu as well as Xuehao Zheng from ZKKF(Beijing) Science & Technology Co. Ltd for the TEM measurement, Gert Wiese as well as Petra Fischer for SEM and hardness measurement and Yunting Li from the Instrument Analysis Center of Shanghai Jiao Tong University (China) for SEM measurement. Lixiang Yang also gratefully thanks the China Scholarship Council (201906230111) for awarding a fellowship to support his study stay at Helmholtz-Zentrum Geesthacht.

PY - 2023/8/1

Y1 - 2023/8/1

N2 - In order to improve the ductility of commercial WE43 alloy and reduce its cost, a Mg-3Y-2Gd-1Nd-0.4Zr alloy with a low amount of rare earths was developed and prepared by sand casting with a differential pressure casting system. Its microstructure, mechanical properties and fracture behaviors in the as-cast, solution-treated and as-aged states were evaluated. It is found that the aged alloy exhibited excellent comprehensive mechanical properties owing to the fine dense plate-shaped β' precipitates formed on prismatic habits during aging at 200 °C for 192 hrs after solution-treated at 500 °C for 24 hrs. Its ultimate tensile strength, yield strength, and elongation at ambient temperature reach to 319 ± 10 MPa, 202 ± 2 MPa and 8.7 ± 0.3% as well as 230 ± 4 MPa, 155 ± 1 MPa and 16.0 ± 0.5% at 250 °C. The fracture mode of as-aged alloy was transferred from cleavage at room temperature to quasi-cleavage and ductile fracture at the test temperature 300 °C. The properties of large-scale components fabricated using the developed Mg-3Y-2Gd-1Nd-0.4Zr alloy are better than those of commercial WE43 alloy, suggesting that the new developed alloy is a good candidate to fabricate the large complex thin-walled components.

AB - In order to improve the ductility of commercial WE43 alloy and reduce its cost, a Mg-3Y-2Gd-1Nd-0.4Zr alloy with a low amount of rare earths was developed and prepared by sand casting with a differential pressure casting system. Its microstructure, mechanical properties and fracture behaviors in the as-cast, solution-treated and as-aged states were evaluated. It is found that the aged alloy exhibited excellent comprehensive mechanical properties owing to the fine dense plate-shaped β' precipitates formed on prismatic habits during aging at 200 °C for 192 hrs after solution-treated at 500 °C for 24 hrs. Its ultimate tensile strength, yield strength, and elongation at ambient temperature reach to 319 ± 10 MPa, 202 ± 2 MPa and 8.7 ± 0.3% as well as 230 ± 4 MPa, 155 ± 1 MPa and 16.0 ± 0.5% at 250 °C. The fracture mode of as-aged alloy was transferred from cleavage at room temperature to quasi-cleavage and ductile fracture at the test temperature 300 °C. The properties of large-scale components fabricated using the developed Mg-3Y-2Gd-1Nd-0.4Zr alloy are better than those of commercial WE43 alloy, suggesting that the new developed alloy is a good candidate to fabricate the large complex thin-walled components.

KW - Ductility

KW - Large-scale sand-cast

KW - Magnesium alloy

KW - WE43

KW - Engineering

UR - http://www.scopus.com/inward/record.url?scp=85114443734&partnerID=8YFLogxK

UR - https://www.mendeley.com/catalogue/e53b753a-8258-318a-8acc-ab5250018731/

U2 - 10.1016/j.jma.2021.08.010

DO - 10.1016/j.jma.2021.08.010

M3 - Journal articles

AN - SCOPUS:85114443734

VL - 11

SP - 2763

EP - 2775

JO - Journal of Magnesium and Alloys

JF - Journal of Magnesium and Alloys

SN - 2213-9567

IS - 8

ER -

DOI