Hot deformation behavior of Mg-2Sn-2Ca alloy in as-cast condition and after homogenization
Publikation: Beiträge in Zeitschriften › Zeitschriftenaufsätze › Forschung › begutachtet
Authors
The hot deformation behavior of Mg-2Sn-2Ca (TX22) alloy has been characterized in the temperature range 300-500°C and strain rate range 0.0003-10s-1 using isothermal constant true strain rate tests. A processing map has been developed on the basis of flow stress data obtained as a function of temperature and strain rate, which revealed two windows or domains for hot working the alloy: (1) 300-370°C/0.0003-0.001s-1 and (2) 400-500°C/0.005-1s-1. Microstructural observations indicated that dynamic recrystallization occurs in both these windows with a finer resulting grain size in the first window. Apparent activation energy values of 183 and 178kJ/mole have been estimated in these windows, respectively and these are much higher than that for self-diffusion in Mg suggesting that considerable back stress is being generated due to the intermetallic particles (CaMgSn) present in the matrix. The mechanisms involving basal+prismatic slip and recovery by climb in the first domain and that of second order pyramidal slip and softening by cross-slip in the second domain are suggested to be occurring in these two domains. The processing map obtained on homogenized alloy is identical to that of the as-cast alloy suggesting that there is no benefit of homogenization treatment as regards hot workability and this is attributed to the thermal stability of the as-cast microstructure.
| Originalsprache | Englisch |
|---|---|
| Zeitschrift | Materials Science and Engineering A |
| Jahrgang | 552 |
| Seiten (von - bis) | 444-450 |
| Anzahl der Seiten | 7 |
| ISSN | 0921-5093 |
| DOIs | |
| Publikationsstatus | Erschienen - 30.08.2012 |
| Extern publiziert | Ja |
- Ingenieurwissenschaften