T1 - Residual stresses near the hot sprues of as-cast Mg-Zn alloys investigated by STRESS-SPEC neutron diffractometer

AU - Gan, Wei Min

AU - Huang, Yuan Ding

AU - Wang, Zhi

AU - Hort, Norbert

AU - Hofmann, Michael

N1 - Conference code: 9

PY - 2014

Y1 - 2014

N2 - Residual strains near the sprues of ingots with different contents of Zn (6 wt. % and 9 wt. %) were measured using neutron diffraction. The results showed that the increase of Zn content decreases the residual stress in the hot sprue region. These results are in good agreement with those obtained by the measurement of hot tearing susceptibility.

AB - Residual strains near the sprues of ingots with different contents of Zn (6 wt. % and 9 wt. %) were measured using neutron diffraction. The results showed that the increase of Zn content decreases the residual stress in the hot sprue region. These results are in good agreement with those obtained by the measurement of hot tearing susceptibility.

KW - Hot sprue

KW - Hot tearing

KW - Magnesium alloy

KW - Residual stress

KW - Solidification

KW - Engineering

UR - http://www.scopus.com/inward/record.url?scp=84886044234&partnerID=8YFLogxK

UR - https://www.mendeley.com/catalogue/5c2c17ef-d9cc-36f9-aaf9-2a872432c0b2/

U2 - 10.4028/www.scientific.net/MSF.768-769.428

DO - 10.4028/www.scientific.net/MSF.768-769.428

M3 - Article in conference proceedings

AN - SCOPUS:84886044234

SN - 9783037858493

T3 - Materials Science Forum

SP - 428

EP - 432

BT - International Conference on Residual Stresses 9 (ICRS 9)

A2 - Kurz, S. J. B.

A2 - Mittemeijer, E. J.

A2 - Scholtes, B.

PB - Trans Tech Publications Ltd

T2 - 9th International Conference on Residual Stresses, ICRS 2012

Y2 - 7 October 2012 through 9 October 2012

ER -