Hot tearing susceptibility of magnesium-gadolinium binary alloys

Publikation: Beiträge in ZeitschriftenZeitschriftenaufsätzeForschungbegutachtet

Standard

Hot tearing susceptibility of magnesium-gadolinium binary alloys. / Srinivasan, Amirthalingam; Wang, Zhi; Huang, Yuanding et al.
in: Transactions of the Indian Institute of Metals, Jahrgang 65, Nr. 6, 12.2012, S. 701-706.

Publikation: Beiträge in ZeitschriftenZeitschriftenaufsätzeForschungbegutachtet

Harvard

APA

Vancouver

Srinivasan A, Wang Z, Huang Y, Beckmann F, Kainer KU, Hort N. Hot tearing susceptibility of magnesium-gadolinium binary alloys. Transactions of the Indian Institute of Metals. 2012 Dez;65(6):701-706. doi: 10.1007/s12666-012-0210-1

Bibtex

@article{4de325468a7e4598a41a6b2beb0d9803,
title = "Hot tearing susceptibility of magnesium-gadolinium binary alloys",
abstract = "Hot tearing susceptibility of Mg-Gd alloys are investigated using instrumented constrained rod casting (CRC) apparatus, and found that the susceptibility increases with increase in Gd content, and reaches a maximum at 2 % after which it decreases to a minimum with 10 % Gd. The high susceptibility observed with 2 % Gd is due to its columnar structure and low amount of eutectic liquid at the time of cracking, whereas equiaxed grain and high liquid content which facilitates crack healing are the reasons for the low susceptibility of Mg-10 Gd alloy.",
keywords = "Crack healing, Grain structure, Hot tearing, Mg-Gd alloys, Solid fraction, Engineering",
author = "Amirthalingam Srinivasan and Zhi Wang and Yuanding Huang and Felix Beckmann and Kainer, {Karl Ulrich} and Norbert Hort",
year = "2012",
month = dec,
doi = "10.1007/s12666-012-0210-1",
language = "English",
volume = "65",
pages = "701--706",
journal = "Transactions of the Indian Institute of Metals",
issn = "0972-2815",
publisher = "Springer",
number = "6",

}

RIS

TY - JOUR

T1 - Hot tearing susceptibility of magnesium-gadolinium binary alloys

AU - Srinivasan, Amirthalingam

AU - Wang, Zhi

AU - Huang, Yuanding

AU - Beckmann, Felix

AU - Kainer, Karl Ulrich

AU - Hort, Norbert

PY - 2012/12

Y1 - 2012/12

N2 - Hot tearing susceptibility of Mg-Gd alloys are investigated using instrumented constrained rod casting (CRC) apparatus, and found that the susceptibility increases with increase in Gd content, and reaches a maximum at 2 % after which it decreases to a minimum with 10 % Gd. The high susceptibility observed with 2 % Gd is due to its columnar structure and low amount of eutectic liquid at the time of cracking, whereas equiaxed grain and high liquid content which facilitates crack healing are the reasons for the low susceptibility of Mg-10 Gd alloy.

AB - Hot tearing susceptibility of Mg-Gd alloys are investigated using instrumented constrained rod casting (CRC) apparatus, and found that the susceptibility increases with increase in Gd content, and reaches a maximum at 2 % after which it decreases to a minimum with 10 % Gd. The high susceptibility observed with 2 % Gd is due to its columnar structure and low amount of eutectic liquid at the time of cracking, whereas equiaxed grain and high liquid content which facilitates crack healing are the reasons for the low susceptibility of Mg-10 Gd alloy.

KW - Crack healing

KW - Grain structure

KW - Hot tearing

KW - Mg-Gd alloys

KW - Solid fraction

KW - Engineering

UR - http://www.scopus.com/inward/record.url?scp=84897072534&partnerID=8YFLogxK

U2 - 10.1007/s12666-012-0210-1

DO - 10.1007/s12666-012-0210-1

M3 - Journal articles

AN - SCOPUS:84897072534

VL - 65

SP - 701

EP - 706

JO - Transactions of the Indian Institute of Metals

JF - Transactions of the Indian Institute of Metals

SN - 0972-2815

IS - 6

ER -

DOI

Zuletzt angesehen

Publikationen

  1. Verfassungsreformen in der Bundesrepublik Deutschland: 1969 – 1994 – 2006
  2. Vertical emission profiles for Europe based on plume rise calculations
  3. Ökologische Nachhaltigkeit durch zivilgesellschaftliche Partizipation?
  4. Extrusion Benchmark 2009 – A Step Ahead in Virtual Process Optimization
  5. Dynamic material flow analysis in the life cycle assessment tool chain
  6. 5. Workshop Umweltinformatik zwischen Nachhaltigkeit und Wandel (UINW 2017)
  7. Simulation of stresses during casting of binary magnesium-aluminum alloys
  8. Implications of Material Flow Cost Accounting for Life Cycle Engineering
  9. Einheitlich, übersichtlich, transparent: Zur Reform der Parteienfinanzierung
  10. A System for Clearance Measurement of Bearings before and after Assembling
  11. Gaussian processes for dispatching rule selection in production scheduling
  12. An analytical approach to evaluating nonmonotonic functions of fuzzy numbers
  13. Thermo-mechanical processing of aluminum profiles subsequent to hot extrusion
  14. Compression creep at 240°C of extruded magnesium alloys containing gadolinium
  15. Improving the identification of mismatches in ecosystem services assessments
  16. Interference of magnesium corrosion with tetrazolium-based cytotoxicity assays
  17. Extrusion benchmark 2009 experimental analysis of deflection in extrusion dies
  18. Die Kooperationsbeziehung zwischen freien Journalisten und ihren Auftraggebern
  19. A plea for a behavioural approach in the science of human resources management
  20. The Influence of Wall Thickness on Hollow Lateral Extrusion of Tubular Billets
  21. Distortion related aspects of cold forging as part of the manufacturing process
  22. Mechanical behaviour and corrosion performance of thin film magnesium WE alloys
  23. Virtuelle Organisationen unter besonderer Berücksichtigung kultureller Barrieren
  24. Influence of cerium on the formation of micro-galvanic corrosion elements of AZ91
  25. Safeguards, financing, and employment in Chinese infrastructure projects in Africa