Characterization of an extruded Mg-Dy-Nd alloy during stress corrosion with C-ring tests

Publikation: Beiträge in ZeitschriftenZeitschriftenaufsätzeForschungbegutachtet

Standard

Characterization of an extruded Mg-Dy-Nd alloy during stress corrosion with C-ring tests. / Maier, Petra; Clausius, Benjamin; Wicke, Jens et al.
in: Metals, Jahrgang 10, Nr. 5, 584, 05.2020.

Publikation: Beiträge in ZeitschriftenZeitschriftenaufsätzeForschungbegutachtet

Harvard

APA

Vancouver

Maier P, Clausius B, Wicke J, Hort N. Characterization of an extruded Mg-Dy-Nd alloy during stress corrosion with C-ring tests. Metals. 2020 Mai;10(5):584. doi: 10.3390/met10050584

Bibtex

@article{f8b61d1d6124492b8f320ac42bdfef02,
title = "Characterization of an extruded Mg-Dy-Nd alloy during stress corrosion with C-ring tests",
abstract = "This study focuses on the characterization of the failure behavior of an extruded Mg10Dy1Nd alloy during stress corrosion. The microstructure, hardness, strength and corrosion behavior of binary alloys Mg10Dy and Mg1Nd are compared to those of the ternary alloy system. The ternary alloy Mg-Dy-Nd that is not fully recrystallized has the highest hardness but lacks ductility. The investigated alloys twin during plastic deformation. Static C-ring tests in Ringer solution were used to evaluate the stress corrosion properties, and stress corrosion could not be found. None of the alloys failed by fracturing, but corrosion pits formed to various extents. These corrosion pits were elliptical in shape and located below the surface. Some of the pits reduced the remaining wall thickness significantly, but the stress increased by the notch effect did not lead to crack initiation. Furthermore, the C-ring specimen was subjected to compressive loading until fracture. Whereas the Mg1Nd alloy showed ductile behavior, the alloys containing Dy fractured on the tensile side. The crack initiation and growth were mainly influenced by the twin boundaries. The Mg10Dy1Nd alloy had an inhomogeneous microstructure and low ductility, which resulted in a lower fracture toughness than that of the Mg10Dy alloy. There were features that indicate hydrogen-assisted fracture. Although adding Nd decreased the fracture toughness, it reduced the grain size and had a positive influence on the corrosion rate during immersion testing.",
keywords = "C-ring test, Corrosion morphology, Magnesium, Mg-Dy-Nd, Stress corrosion, Engineering",
author = "Petra Maier and Benjamin Clausius and Jens Wicke and Norbert Hort",
note = "The authors acknowledge S{\"o}ren M{\"u}ller (Extrusion Research and Development Center TU Berlin) for extruding the tubes and the support of Hartmut Habeck (University of Applied Sciences Stralsund) for the corrosion measurements. Furthermore, David Barkowsky, Fabian Landt and Jan-Malte Kapust (University of Applied Sciences Stralsund) are thanked for supporting the mechanical testing, metallographic work and corrosion experiments.",
year = "2020",
month = may,
doi = "10.3390/met10050584",
language = "English",
volume = "10",
journal = "Metals",
issn = "2075-4701",
publisher = "MDPI AG",
number = "5",

}

RIS

TY - JOUR

T1 - Characterization of an extruded Mg-Dy-Nd alloy during stress corrosion with C-ring tests

AU - Maier, Petra

AU - Clausius, Benjamin

AU - Wicke, Jens

AU - Hort, Norbert

N1 - The authors acknowledge Sören Müller (Extrusion Research and Development Center TU Berlin) for extruding the tubes and the support of Hartmut Habeck (University of Applied Sciences Stralsund) for the corrosion measurements. Furthermore, David Barkowsky, Fabian Landt and Jan-Malte Kapust (University of Applied Sciences Stralsund) are thanked for supporting the mechanical testing, metallographic work and corrosion experiments.

PY - 2020/5

Y1 - 2020/5

N2 - This study focuses on the characterization of the failure behavior of an extruded Mg10Dy1Nd alloy during stress corrosion. The microstructure, hardness, strength and corrosion behavior of binary alloys Mg10Dy and Mg1Nd are compared to those of the ternary alloy system. The ternary alloy Mg-Dy-Nd that is not fully recrystallized has the highest hardness but lacks ductility. The investigated alloys twin during plastic deformation. Static C-ring tests in Ringer solution were used to evaluate the stress corrosion properties, and stress corrosion could not be found. None of the alloys failed by fracturing, but corrosion pits formed to various extents. These corrosion pits were elliptical in shape and located below the surface. Some of the pits reduced the remaining wall thickness significantly, but the stress increased by the notch effect did not lead to crack initiation. Furthermore, the C-ring specimen was subjected to compressive loading until fracture. Whereas the Mg1Nd alloy showed ductile behavior, the alloys containing Dy fractured on the tensile side. The crack initiation and growth were mainly influenced by the twin boundaries. The Mg10Dy1Nd alloy had an inhomogeneous microstructure and low ductility, which resulted in a lower fracture toughness than that of the Mg10Dy alloy. There were features that indicate hydrogen-assisted fracture. Although adding Nd decreased the fracture toughness, it reduced the grain size and had a positive influence on the corrosion rate during immersion testing.

AB - This study focuses on the characterization of the failure behavior of an extruded Mg10Dy1Nd alloy during stress corrosion. The microstructure, hardness, strength and corrosion behavior of binary alloys Mg10Dy and Mg1Nd are compared to those of the ternary alloy system. The ternary alloy Mg-Dy-Nd that is not fully recrystallized has the highest hardness but lacks ductility. The investigated alloys twin during plastic deformation. Static C-ring tests in Ringer solution were used to evaluate the stress corrosion properties, and stress corrosion could not be found. None of the alloys failed by fracturing, but corrosion pits formed to various extents. These corrosion pits were elliptical in shape and located below the surface. Some of the pits reduced the remaining wall thickness significantly, but the stress increased by the notch effect did not lead to crack initiation. Furthermore, the C-ring specimen was subjected to compressive loading until fracture. Whereas the Mg1Nd alloy showed ductile behavior, the alloys containing Dy fractured on the tensile side. The crack initiation and growth were mainly influenced by the twin boundaries. The Mg10Dy1Nd alloy had an inhomogeneous microstructure and low ductility, which resulted in a lower fracture toughness than that of the Mg10Dy alloy. There were features that indicate hydrogen-assisted fracture. Although adding Nd decreased the fracture toughness, it reduced the grain size and had a positive influence on the corrosion rate during immersion testing.

KW - C-ring test

KW - Corrosion morphology

KW - Magnesium

KW - Mg-Dy-Nd

KW - Stress corrosion

KW - Engineering

UR - http://www.scopus.com/inward/record.url?scp=85084995114&partnerID=8YFLogxK

U2 - 10.3390/met10050584

DO - 10.3390/met10050584

M3 - Journal articles

AN - SCOPUS:85084995114

VL - 10

JO - Metals

JF - Metals

SN - 2075-4701

IS - 5

M1 - 584

ER -

DOI